However, collapsible totes are an alternative style of tote gaining traction as a more efficient, eco-conscious solution.

The Solution  

The Solution  

The Solution  

The Solution

Added to the feed throat and designed to increase the polymer chain length via reactive extrusion, rePrize enables an increase in both the polymer intrinsic and melt viscosity. FEATURE BENEFIT • Liquid technology • More accurate dose control • Less variation in melt flow and product IV • Can be coupled to an on-line rheometer • Shorter transition times • Does not require pre-drying • Less dust • Higher IV in melt phase • Improved uniformity when replacing virgin PET in PCR sheet • Eliminate/reduce solid phase polymerization (rPET) • Increased use of post consumer flake or re-grind (Sheet) • Reduced brittleness, less breakages and scrap • More consistent melt flow • Reduced cost • Higher productivity • Cleaner working environment PROCESS HIGHLIGHTS • Higher productivity • Cleaner working environment • New product designs and applications • Improved shelf appeal PET SHEET • Increases final IV • Less variation in product IV • More consistent melt flow • Increased use of flake or regrind • Shorter transition times • Reduced scrap • Reduced dust • Improved impact strength • Improved low temperature performance • Improved aesthetics Information and photographs supplied by Sunwell Global Ltd • Higher productivity • Improved sustainability • Lighter weight, higher strength • Properties comparable to PS packaging • Recyclable PET MONO/MULTI LAYERED SHEET XPET FOAM SHEET ROUND DIE • Improved melt flow consistency • Improved IV consistency • Increased recycle content • Reduced rejects and scrap • Increased product strength • Improved low temperature performance • Increase final IV • Increased use of regrind • Impossible to start up without it • Faster product changeover • Easier to cut • Increased strength • Lighter weight • Good sealing ColorMatrix™ rePrize is a PET compatible formulated liquid dispersion, designed to increase the polymer chain length via reactive extrusion. This results in an increase in both the polymer intrinsic and melt viscosity. rePrize is suited to applications in: • PET monolayer sheet • PET multilayered sheet • PET foamed sheet rePrize can be used to optimise sheet manufacturing processes and product quality, whilst allowing for increased levels of recycle, contributing towards improved sustainability and reduced costs PRODUCT DESCRIPTION GLOBAL REGULATORY APPROVALS PRODUCT FDA EU GB MERCOSUR rePrize • • • • 1.844.4AVIENT www.avient.com Copyright © 2020, Avient Corporation.

BASE RESIN PPA PC PSU PES PPS CO- POLYMER ACETAL PEEK PA Barrel Temperatures* °F (°C) Rear Zone 550–580 (288–305) 520–560 (271–293) 600–640 (316–338) 630–660 (332–338) 550–580 (288–304) 350–370 (177–188) 660–700 (349–371) 440–490 (227–254) Center Zone 560–600 (293–316) 530–570 (277–299) 620–670 (327–354) 650–680 (343–360) 560–615 (293–324) 380–390 (193–200) 700–730 (371–388) 470–510 (243–266) Front Zone 580–620 (304–327) 550–580 (288–305) 630–680 (332–360) 670–730 (354–388) 590–630 (310–332) 390–430 (200–221) 720–750 (382–400) 490–540 (254–282) Nozzle 575–615 (302–324) 550–600 (288–316) 630–680 (332–360) 680–700 (360–371) 600–625 (316–330) 380–415 (193–213) 720–750 (382–400) 520–570 (271–300) Melt Temperature 575–615 (302–324) 560–600 (293–316) 625–675 (330–358) 650–710 (343–377) 600–625 (316–330) 370–410 (188–210) 670–740 (354–393) 520–570 (271–300) Mold Temperature 250–300 (121–150) 175–240 (80–116) 190–300 (88–150) 225–325 (107–164) 250–325 (121–164) 150–225 (66–107) 290–375 (143–190) 150–200 (66–93) Pack & Hold Pressure 50%–75% of Injection Pressure Injection Velocity in/s 1.0–3.0 Back Pressure psi 50 Screw Speed rpm 50–90 Drying Parameters °F (°C) 6 hrs @ 175 (80) 4 hrs @ 250 (121) 4 hrs @ 275 (135) 4 hrs @ 300 (150) 4 hrs @ 250 (121) 2 hrs @ 200 (93) 3 hrs @ 300 (150) 4 hrs @ 180 (82) Allowable Moisture % < 0.05 < 0.02 < 0.02 < 0.04 < 0.02 0.15–0.20 < 0.02 0.10–0.20 Cushion in 0.125–0.250 Screw Compression Ratio 2.5:1–3.5:1 2.0:1–2.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 Nozzle Type General General General General General General General Reverse Taper Clamp Pressure 5–6 Tons/in2 of projected area of cavities and runner system * Barrel temperatures should be elevated for compounds designed for electrical insulative properties. PROBLEM CAUSE SOLUTION Incomplete Fill Melt and/or mold temperature too cold Shot Size • Increase nozzle and barrel temperatures • Increase mold temperature • Increase injection speed • Increase pack and hold pressure • Increase nozzle tip diameter • Check thermocouples and heater bands • Enlarge or widen vents and increase number of vents • Check that vents are unplugged • Check that gates are unplugged • Enlarge gates and/or runners • Perform short shots to determine fill pattern and verify proper vent location • Increase wall thickness to move gas trap to parting line • Increase cushion Brittleness Melt temperature too low Degraded/Overheated material Gate location and/or size • Increase melt temperature • Increase injection speed • Measure melt temperature with pyrometer • Decrease melt temperature • Decrease back pressure • Use smaller barrel/excessive residence time • Relocate gate to nonstress area • Increase gate size to allow higher flow speed and lower molded-in stress Fibers on Surface (Splay) Melt temperature too low Insufficient packing • Increase melt temperature • Increase mold temperature • Increase injection speed • Increase pack and hold pressure, and time Sink Marks Part geometry too thick Melt temperature too hot Insufficient material volume • Reduce wall thickness • Reduce rib thickness • Decrease nozzle and barrel temperatures • Increase shot size • Increase injection rate • Increase packing pressure Flash Injection pressure too high Excess material volume Melt and/or mold temperature too hot • Decrease injection pressure • Increase clamp pressure • Decrease injection speed • Increase transfer position • Decrease pack pressure • Decrease shot size • Decrease injection speed • Decrease nozzle and barrel temperatures • Decrease mold temperature • Decrease screw speed TROUBLESHOOTING RECOMMENDATIONS PROBLEM CAUSE SOLUTION Excessive Shrink Too much orientation • Increase packing time and pressure • Increase hold pressure • Decrease melt temperature • Decrease mold temperature • Decrease injection speed • Decrease screw rpm • Increase venting • Increase cooling time Not Enough Shrink Too little orientation • Decrease packing pressure and time • Decrease hold pressure • Increase melt temperature • Increase mold temperature • Increase injection speed • Increase screw rpm • Decrease cooling time Burning Melt and/or mold temperature too hot Mold design Moisture • Decrease nozzle and barrel temperatures • Decrease mold temperature • Clean, widen and increase number of vents • Increase gate size or number of gates • Verify material is dried at proper conditions Nozzle Drool Nozzle temperature too hot • Decrease nozzle temperature • Decrease back pressure • Increase screw decompression • Verify material has been dried at proper conditions Weld Lines Melt front temperatures too low • Increase pack and hold pressure • Increase melt temperature • Increase vent width and locations • Increase injection speed • Decrease injection speed • Increase gate size • Perform short shots to determine fill pattern and verify proper vent location • Add vents and/or false ejector pin • Move gate location Warp Excessive orientation • Increase cooling time • Increase melt temperature • Decrease injection pressure and injection speed • Increase number of gates Sticking in Mold Cavities are overpacked Part is too hot • Decrease injection speed and pressure • Decrease pack and hold pressure • Decrease nozzle and barrel temperatures • Decrease mold temperature • Increase cooling time • Increase draft angle • Decrease nozzle and barrel temperatures • Decrease mold temperature TROUBLESHOOTING RECOMMENDATIONS Note: These are general processing conditions.

Base Resin PPA PC PSU PES PPS Co- polymer Acetal PEEK PA Barrel Temperatures* °F (°C) Rear Zone 550–580 (288–305) 550–590 (288–310) 600–640 (316–338) 630–660 (332–338) 550–580 (288–304) 350–370 (177–188) 660–700 (349–371) 440–490 (227–254) Center Zone 560–600 (293–316) 570–600 (300–316) 620–670 (327–354) 650–680 (343–360) 560–615 (293–324) 380–390 (193–200) 700–730 (371–388) 470–510 (243–266) Front Zone 580–620 (304–327) 580–630 (304–322) 630–680 (332–360) 670–730 (354–388) 590–630 (310–332) 390–430 (200–221) 720–750 (382–400) 490–540 (254–282) Nozzle 575–615 (302–324) 580–630 (304–322) 630–680 (332–360) 680–700 (360–371) 600–625 (316–330) 380–415 (193–213) 720–750 (382–400) 520–570 (271–300) Melt Temperature 575–615 (302–324) 580–625 (304–330) 625–675 (330–358) 650–710 (343–377) 600–625 (316–330) 370–410 (188–210) 670–740 (354–393) 520–570 (271–300) Mold Temperature 250–300 (121–150) 175–240 (80–116) 190–300 (88–150) 225–325 (107–164) 250–325 (121–164) 190–250 (88–121) 290–375 (143–190) 150–200 (66–93) Pack & Hold Pressure 50%–75% of Injection Pressure Injection Velocity in/s 1.0–3.0 Back Pressure psi 50 Screw Speed rpm 50–90 Drying Parameters °F (°C) 6 hrs @ 175 (80) 4 hrs @ 250 (121) 4 hrs @ 275 (135) 4 hrs @ 250 (121) 3 hrs @ 300 (150) 2 hrs @ 200 (93) 3 hrs @ 275 (135) 4 hrs @ 180 (82) Cushion in 0.125–0.250 Screw Compression Ratio 2.5:1–3.5:1 2.0:1–2.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 2.5:1–3.5:1 Nozzle Type General General General General General General General Reverse Taper Clamp Pressure 5–6 Tons/in2 of projected area of cavities and runner system * Barrel temperatures should be elevated for compounds designed for electrical insulative properties. PROBLEM CAUSE SOLUTION Excessive Shrink Too much orientation • Increase packing time and pressure • Increase hold pressure • Decrease melt temperature • Decrease mold temperature • Decrease injection speed • Decrease screw rpm • Increase venting • Increase cooling time Not Enough Shrink Too little orientation • Decrease packing pressure and time • Decrease hold pressure • Increase melt temperature • Increase mold temperature • Increase injection speed • Increase screw rpm • Decrease cooling time Burning Melt and/or mold temperature too hot Mold design Moisture • Decrease nozzle and barrel temperatures • Decrease mold temperature • Clean, widen and increase number of vents • Increase gate size or number of gates • Verify material is dried at proper conditions Nozzle Drool Nozzle temperature too hot • Decrease nozzle temperature • Decrease back pressure • Increase screw decompression • Verify material has been dried at proper conditions Weld Lines Melt front temperatures too low • Increase pack and hold pressure • Increase melt temperature • Increase vent width and locations • Increase injection speed • Decrease injection speed • Increase gate size • Perform short shots to determine fill pattern and verify proper vent location • Add vents and/or false ejector pin • Move gate location Warp Excessive orientation • Increase cooling time • Increase melt temperature • Decrease injection pressure and injection speed • Increase number of gates Sticking in Mold Cavities are overpacked Part is too hot • Decrease injection speed and pressure • Decrease pack and hold pressure • Decrease nozzle and barrel temperatures • Decrease mold temperature • Increase cooling time • Increase draft angle • Decrease nozzle and barrel temperatures • Decrease mold temperature TROUBLESHOOTING RECOMMENDATIONS PROBLEM CAUSE SOLUTION Incomplete Fill Melt and/or mold temperature too cold Shot Size • Increase nozzle and barrel temperatures • Increase mold temperature • Increase injection speed • Increase pack and hold pressure • Increase nozzle tip diameter • Check thermocouples and heater bands • Enlarge or widen vents and increase number of vents • Check that vents are unplugged • Check that gates are unplugged • Enlarge gates and/or runners • Perform short shots to determine fill pattern and verify proper vent location • Increase wall thickness to move gas trap to parting line • Increase cushion Brittleness Melt temperature too low Degraded/Overheated material Gate location and/or size • Increase melt temperature • Increase injection speed • Measure melt temperature with pyrometer • Decrease melt temperature • Decrease back pressure • Use smaller barrel/excessive residence time • Relocate gate to nonstress area • Increase gate size to allow higher flow speed and lower molded-in stress Fibers on Surface (Splay) Melt temperature too low Insufficient packing • Increase melt temperature • Increase mold temperature • Increase injection speed • Increase pack and hold pressure, and time Sink Marks Part geometry too thick Melt temperature too hot Insufficient material volume • Reduce wall thickness • Reduce rib thickness • Decrease nozzle and barrel temperatures • Increase shot size • Increase injection rate • Increase packing pressure Flash Injection pressure too high Excess material volume Melt and/or mold temperature too hot • Decrease injection pressure • Increase clamp pressure • Decrease injection speed • Increase transfer position • Decrease pack pressure • Decrease shot size • Decrease injection speed • Decrease nozzle and barrel temperatures • Decrease mold temperature • Decrease screw speed TROUBLESHOOTING RECOMMENDATIONS www.avient.com Copyright © 2020, Avient Corporation.

HIPS POLYMER 15 MF PULVERIZED

PB 120 TYPE CO-POLYMER