FIBER-LINE™ High Performance Synthetic Fibers PRODUCT SELECTION GUIDE FIBER-LINE™ HIGH PERFORMANCE SYNTHETIC FIBERS Kevlar® Para-Aramid Nomex® Meta-Aramid Vectran® LCP Zylon® PBO Carbon Fiber UHMWPE PET Polyester Fiberglass Novoloid Technora® Filament Yarn TECHNICAL PROPERTIES Standard High Modulus Standard Standard High Standard High Standard Standard High High Tenacity Low Shrink E-Glass S-Glass Standard Standard Breaking Tenacity (g/d) 23.0 23.6 5.0 23.0 30.0 42.0 42.0 23.0 28.0 38 9.3 8.4 6.0 - 7.3 6.7 - 9.4 1.5 28.0 Specific Gravity (Ratio) 1.44 1.44 1.38 1.40 1.40 1.54 1.56 1.80 0.97 0.97 1.38 1.38 2.58 2.48 1.27 1.39 Elongation at Break (%) 3.5 2.5 30.0 3.8 2.8 3.5 2.5 1.5 3.5 3.1 14.6 19.5 3.5 5.5 30.0 - 40.0 4.6 Tensile Modulus (g/d) 555 885 125 600 830 1200 1800 1480 850 1250 120 70 200–275 140–170 2.5–5.0 590 Equilibrium Moisture Regain at 55% RH (%) 5.0 5.0 4.5

Matrix Resin Fiber Reinforcement Fiber Content, by Weight (%) Epoxy E-CR or E-Glass >70% MATERIAL TECHNICAL DATA Property Test Procedure Rod Diameter 1.25 in (31.75 mm) 1.50 in (38.10 mm) Glass Transition Temp (Tg) ASTM 1356 100°C Minimum 100°C Minimum Water Absorption 24 hours at 50°C (122°F) ASTM D570 0.03% 0.03% Short Beam Strength (ILSS) ASTM 2344 8,400 psi (58 MPa) 9,200 psi (64 MPa) Transverse Shear Strength ASTM 7617 23,400 psi (160 MPa) 24,640 psi (170 MPa) Traceability Lot number shall be clearly marked on each package/shipment.

PRODUCT FR™ 0521-48 R1 FR™ 0587-21 R3 TYPE LSFOH PP ✔ Halogenated FR PP ✔ APPLICATION Crossweb ✔ ✔ Insulation ✔ GENERAL PROPERTIES Specific gravity g/cm3 1.50 1.46 LOI % 31 34 Tensile Strength MPa 13.8 15.9 Elongation % 320 320 Dielectric constant 1MHz 3.06 2.88 Shore D - 72 75.6 T°C max/T°F Max °C/°F 232/450 232/450 FIRE PERFORMANCE UL 444 ✔ ✔ Plenum yellow card ✔ ✔

Wide range of standard grades and customized formulations to meet your requirements

Constructed to provide any facility with the latest in military grade protection from armed attackers

Injection Molding Parameters Base Resin PPA PPS PA 6/6 PA 12 Barrel Temperatures °F (°C)* Rear Zone 550–580 (288–305) 550–580 (288–305) 440–490 (227–254) 440–480 (227–250) Center Zone 560–600 (293–316) 560–615 (293–324) 470–510 (243–266) 460–510 (238–266) Front Zone 580–620 (304–327) 590–630 (310–333) 490–540 (254–282) 480–520 (250–271) Nozzle 575–615 (302 –324) 600–625 (316–330) 520–570 (271–300) 500–530 (260–277) Melt Temperature °F (°C) 575–615 (302–324) 600–625 (316–330) 520–570 (271–300) 500–530 (260–277) Mold Temperature °F (°C) 250–300 (121–150) 250–300 (121–150) 150–200 (66–93) 150–200 (66–93) Pack and Hold Pressure 50–80% of Injection Pressure Injection Velocity 1.0–3.0 in/sec Back Pressure 25–100 psi Screw Speed 25–75 rpm Drying Parameters °F (°C) 6 hours @ 175 (80) 6 hours @ 300 (150) 3 hours @ 180 (82) 3 hours @ 180 (82) Cushion 0.125–0.250 in Screw Compression Ratio 2.5:1–3.5:1 2.0:1–2.5:1 2.5:1–3.5:1 2.5:1–3.5:1 Nozzle Type General Purpose General Purpose Reverse Taper Reverse Taper Clamp Pressure 4–5 tons/in2 of projected area of cavities and runner system * Barrel temperatures should be elevated for compounds designed for electrical insulative properties.

Parameters NM5600-8002 RS NM5600-8004 RS Drying Temperature 100–120°C 100–130°C Drying Time 4–6 hours 4–6 hours Barrel Temperature °C °C Rear Zone 250–270 260–270 Central Zone 260–280 270–290 Front Zone 270–295 290–305 Nozzle 290–300 290–300 Mold Temperature 80–100 80–100 Screw Speed Moderate Moderate Back Pressure 3–10bar 3–10bar Cushion stroke 5–10% of plasticizing stroke 5–10% plasticizing of stroke Injection Speed Medium Medium Injection Pressure Medium–high Medium–high Holding Pressure 30–50% of injection pressure 20–40% of injection pressure Screw Type General purpose General purpose Screw L/D 20:1 20:1 Screw Compression Ratio 2.5:1 2.5:1 Non-return Check Valve Free flow check ring Free flow check ring Nozzle Type Reverse taper Reverse taper Barrel Capacity 30–80% of barrel should be used Processing Guide 2 Start Up & Shut Down Recommendations Purge Compound 1. 2–3 melt flow PP or purging compound.

Bradley C.

c/o

16550 EPIC RIVAL SPORT VICTORY ANTHRA-C